ASTM A240 Grade 301 Stainless Steel Sheet SS Sheet UNS S30100 Thickness 0.3-3.0mm
| Product Name | Stainless Steel Sheet & Plate |
| Thinckness | Cold rolled:0.3mm-3mm Hot rolled: 3.0mm-80mm |
| Standard Size | Cold Rolled 1000*2000mm 1219*2438mm 1500*3000mm |
| Hot Rolled 1500*6000mm 1800*6000mm 2000*6000mm | |
| Service | Cutting (laser cutting, plasma cutting, cutting machine), Bending |
| Surface Service | Raw finishing (2B NO.1) Finishing(HL 8K Checkered.etc) |
| Standard | ASTM, AISI, DIN, EN, GB, JIS |
| Mainly Grade | 200 series: 201, 202 300 series: 301 304 309S 310S 316L 316Ti 317L 321 347 400 series: 409, 409L, 410, 420, 430, 431, 439,441 , 443 , 444 |
| Brand | TISCO BAOSTEEL ZPSS LISCO JISCO |
| Application range | Decoration, Industry ,Kitchenwave ,Building, Elevator |
301 stainless steel sheet is a versatile austenitic steel with high strength and excellent corrosion resistance. Its primary alloying elements are chromium and nickel. It shows up in the aerospace, automotive, architecture, and transportation industries.
This stainless steel grade demonstrates excellent corrosion resistance, high strength, and good ductility. High hardness combined with high strength achieved through cold working make 301 suitable for structural applications in aircraft and its excellent corrosion resistance meet food service equipment standards. It can be easily formed and drawn. This grade is non-hardenable by heat treatment.
| C | MN | P | S | SI | CR | NI | N |
|---|---|---|---|---|---|---|---|
| 0.15% max | 2% max | 0.045% max | 0.03% max | .75% max | 16 - 18% | 6 - 8% | 0.1% max |
| MECHANICAL PROPERTIES | ||
|---|---|---|
| Metric | Imperial | |
| Tensile Strength, Ultimate | 827 MPa | 120 ksi |
| Tensile Strength, Yield | 310 MPa | 45 ksi |
| Elongation at Break (in 2") | 60% | 60% |
| Rockwell Hardness | B86 | B86 |
ANSWER:
The amount of chromium and nickel in 301 stainless steel is lower than in 304. The reduction of chromium and nickel extends the range of cold work-hardening capability which in turn produces higher tensile strengths.
High strength and excellent corrosion resistance make Type 301 Stainless Steel useful for a wide variety of applications. Typical uses include: