AISI410/410S Stainless Steel Strip ASTM A240 Thickness 0.3 - 3.0mm Cold Rolled from TISCO
| Product Name | Stainless Steel Strips |
| Length | As required |
| Width | 3mm-1219mm or as required |
| Thickness | 0.1mm-6.0mm or as required |
| Standard | AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
| Technique | Hot rolled / cold rolled |
| Surface Treatment | 2B or according to customer requirement |
| Thickness tolerance | ±0.01mm |
| Material | 201, 202, 301, 302, 303, 304, 304L, 304H, 310S, 316, 316L, 317L, 321,310S 309S, 409L ,410, 410S,420, 430, 431, 440A,904L |
| Application | It is widely used in high temperature applications, medical devices, building materials, chemistry, food industry, agriculture, ship components.It also applies to food, beverage packaging, kitchen supplies, trains, aircraft, conveyor belts, vehicles, bolts, nuts, springs, and screen. |
| MOQ | 1tons.We also can accept sample order. |
| Shipment time | Within 15-20 workdays after receiving deposit or L/C |
| Export packing | Waterproof paper, and steel strip packed.Standard Export Seaworthy Package.Suit for all kinds of transport,or as required |
| Capacity | 250,000 tons/year |
Grade Specification
| USA | JP | DE | EUR | CN |
|---|---|---|---|---|
| ASTM | JIS | DIN | EN | GB |
| 410S | SUS410S | X6Cr13 | 1.4000 | 06Cr13 |
The typical chemical composition is shown in the table below.
| Grade | Standard | 410S Chemical Composition | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| C | Si | Mn | Cr | Ni | P | S | Mo | Others | ||
| ≤ % | ≤ % | % | % | % | ≤ % | ≤ % | ≤ % | % | ||
| 410S | ASTM A240 | 0.08 | 1.0 | 1.0 | 11.5 - 13.5 | 0.6 | 0.04 | 0.015 | - | - |
| 1.4000 | EN 10088-2 | 0.08 | 1.0 | 1.0 | 12.0 - 14.0 | - | 0.04 | 0.015 | - | - |
| SUS410S | JIS G 4304 | JIS G 4305 | 0.08 | 1.0 | 1.0 | 11.5 - 13.5 | 0.6 | 0.04 | 0.03 | - | - |
The mechanical properties are given in the table below.
| Grade | Standard | 410S Mechanical Properties | ||||
|---|---|---|---|---|---|---|
| Tensile Strength | Yield Strength 0.2% | Elongation >% | Hardness | |||
| (MPa) ≥ | (MPa) ≥ | HRB ≤ | HB ≤ | |||
| 410S | ASTM A240 | 415 | 205 | 19 | 89 | 183 |
| 1.4000 | EN 10088-2 | 400-600 | 240 | 19 | - | 200 |
| SUS410S | JIS G 4304 | JIS G 4305 | 410 | 205 | 20 | 88 | 183 |
410S remains soft and ductile even when rapidly cooled from above the critical temperature. This non-hardening characteristic helps prevent cracking when the alloy is exposed to high temperatures or welded.Typical applications include petroleum refining, petrochemical processing,thermal processing , gate valves,press plates , heat exchangers,ore processing and mining machinery.