Alloy 20 Nickel Alloy Round Bar / Nickel Alloy Rod Hot Rolled 10 - 250mm UNS N08020 Alloy
| Form | Nickel Alloy Bars |
| Grade | Alloy 20 |
| Outer Diameter (mm) | 6mm-250mm or according to customer’s requirement |
| Length | 1meter, 3 meters and 6 meters or customer’s requirement |
| Standard | ASTM, ASME, EN, JIS, DIN, GB/T, etc |
| Process Method | Hot Rolled, Cold Drawn, Cold Rolled, Forged Round Bar & Rod |
| Surface Finish | Bright, Hot Rolled Pickled, Cold Drawn, Sand Blasting Finished, Polished, Hairline |
| Other Grade | Hastelloy : B2 B3 C22 C276 G30 X Incoloy: 800 800H 800HT 825 925 A286 330 Inconel: 600 601 617 625 718 725 X-750 Monel: 400 k-500 |
| Price Item | EXW FOB CFR CIF |
| Payment | 30% TT inadvance, 70% TT Balance against copy of B/L |
| Delivery Time | It depends on your bars order total quantity and stock of these mother origin materials. Usually from the start of the order to the completion of production is about 3-4 weeks |
| Quality Requirement | Mill test certificate will be offered with shipment, the third party inspection is available |
| Main Markets | Europe, North America, Middle East, Southeast Asia |
| Metal Test | High or low temperature impact test, metallographic analysis |
| Chemical Analysis | As nickel alloy C276 bars standard |
Alloy 20 (UNS N08020) is an austenitic, nickel-iron-chromium based super alloy with additions of Copper and Molybdenum which provide resistance to hostile environments, pitting, and crevice corrosion. It is also stabilized with Columbium to minimize carbide precipitation during welding. Alloy 20 appears to fall between both the stainless and nickel categories as it contains characteristics of both. It was designed for maximum resistance to acid attack and demonstrates superior resistance to stress-corrosion cracking in boiling 20% to 40% sulfuric acid, and also has excellent general corrosion resistance to sulfuric acid and to chloride stress corrosion cracking. Alloy 20 has good mechanical properties at both ambient and elevated temperatures, up to approximately
930°F (500°C) and is readily fabricated by usual industrial processes.
Specifications: UNS N08020
hemical Properties:
| TYPE | C | Cr | Cu | Fe | Mn | Mo | Ni | P | Si | S | Nb (Cb) |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Alloy 20 UNS N08020 | 0.07 max | min: 19.00 max: 21.00 | min: 3.00 max: 4.00 | Balance | 2.00 max | min: 2.00 max: 3.00 | min: 32.00 max: 38.00 | 0.045 max | 1.00 max | 0.035 max | 8 XC min 1.00 max |
Mechanical Properties:
| Stabilized-Annealed Condition | ||||||
|---|---|---|---|---|---|---|
| Product Form | Tensile Strength, ksi (min) | Yield Strength, 0.2% offset ksi (min) | Elongation % (min) | Reduction of Area % (min) | Hardness Brinell (max) | Hardness Rockwell B (max) |
| Plate, Sheet | 80 | 35 | 30 | — | 217 | 95 |
| Bar | 80 | 35 | 30 | 50 | — | — |
Alloy 20 was originally designed for use in sulfuric acid related applications; however, it is now frequently used in a wide variety of industries. Applications that commonly use Alloy 20 include: