JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
WUXI DETA METAL PRODUCTS CO.,LTD
Add to Cart
| Products | Stainless Steel Plate |
| Thickness | 0.6 - 60.0mm |
| Width | 1000mm 1219mm 1500mm 1800mm 2000mm or other width as request |
| Length | 2000mm 2438mm 3000mm 6000mm or other length as request |
| Grade | 201 202 301 304 304L 304H 309S 310S 310H 316L 316Ti 317L 321 347 409L 410 420 430 431 436L 439 441 443 444 2205 2507 904L 600 625 800 825 718 253MA 254SMO Nitronic 60 925 926.etc |
| Service | Laser Cutting, Surface processing, bending |
| Brand | TISCO BAOSTEEL POSCO LISCO JISCO |
| Standard | ASTM JIS GB DIN EN BS |
| Certificate | ISO MTC C/O F/E |
| Packing | Wooden pallets and waterproof paper |
| Deliver time | 5 - 15 days |
| Loading port | Shanghai Port |
Alloy 925 is a precipitation-hardenable nickel-iron-chromium alloy with added copper and molybdenum. It exhibits high strength and excellent resistance to pitting, crevice corrosion, and stress-corrosion cracking in many aqueous environments containing chlorides and sulfides.
N08925 stainless steel is a superaustenitic (highly alloyed) stainless steel formulated for primary forming into wrought products. Cited properties are appropriate for the annealed condition.
It has a moderately high thermal conductivity and a moderately high ductility among wrought superaustenitic stainless steels.
The following table shows the chemical composition of alloy 925.
| Element | Ni | Fe | Cr | Mo | Ti | Cu | Al | C |
| 925 | 44 | 28 | 21 | 3 | 2.1 | 1.8 | 0.3 | 0.01 |
Welding
Welding of alloy 925 can be performed using gas-tungsten arc welding, shielded metal arc-welding and submerged arc welding.
Forging is performed at temperatures ranging from 927 to 1177°C (1700 to 2150°F).
The alloy is hot-worked in the temperatures ranging from 871 to 982°C (1600 to 1800°F).
Cold working of the alloy can be done using standard tooling. Plain carbon tool steels are not recommended for forming this alloy as they tend to produce galling.
Alloy 925 is annealed at 1010°C (1850°F) for at least 2 h and then air cooled.
The following are some of the major applications of alloy 925: