C11000 ETP Copper Chemical Composition Flat Copper Bar ASTM Standard
| Product name | Copper flat bar |
| Copper and copper alloy grade | C11000,C10100,C12200 H59, H60, H62, H65, H68, H70, H80, H85, H90, H96, C2100, C2200,C2300, C2400, C2600, C2680, C2720, C2800, C3560, C3601, C3713, C3771, C3561 , CuZn30, CuZn32, CuZn35, CuZn37, CuZn40 ,TU1, T2, TP2, H96, H90, H85, H80, H70, H65, H63, H62, H59, HPb63-3, HPb66-0.5, HPb62-2, HPb62-3, HPb59-3, HSn70-1, HSn62-1,QSn8-0.3, QSn4-4-4, QAl9-4, QSB-1 etc. |
| Size | Round Bar: 6mm - 200mm |
| Square Bar: 4x4mm - 200x200mm | |
| Hex Bar: 8x8mm - 100x100mm | |
| Flat Bar: 20x2mm - 200x20mm | |
| Length | 2m,3m,5.8m,6m, or as required. |
| Processing | Extrusion/cold drawn |
| Temper | 1/4 Hard, 1/2 Hard, 3/4 Hard, Hard, Soft |
| Surface finish | Mill,polished,bright,oiled,hair line,brush,mirror,sand blast,or as required. |
Farmers Copper has the following specs for C110 ETP copper in stock:
We can offer material cut to your specifications on our bar saws, shears, precision plate saws, and water jet cut. We service a variety of industries. Please contact one of our knowledgeable sales staff today to help you with your C11000 ETP Copper needs.
(%max., unless shown as range or min.)
| CU(1) | O | |
| Min./Max. | 99.90 min | - |
| Nominal | - | .04 |
| Melting Point – Liquidus ⁰F | 1981 | |
| Melting Point – Solidus ⁰F | 1949 | |
| Density lb/cu in. at 68⁰F | 0.322(1) | |
| Specific Gravity | 8.91 | |
| Electrical Conductivity % IACS at 68⁰F | 101(2) | |
| Thermal Conductivity Btu/sq ft/ft hr/ ⁰F at 68⁰F | 226 | |
| Coefficient of Thermal Expansion 10-6 per ⁰F (68-212 ⁰F) | 9.4 | |
| Coefficient of Thermal Expansion 10-6 per ⁰F (68-392 ⁰F) | 9.6 | |
| Coefficient of Thermal Expansion 10-6 per ⁰F (68-572 ⁰F) | 9.8 | |
| Specific Heat Capacity Btu/lb/⁰F @ 68 ⁰F | 0.092 | |
| Modulus of Elasticity in Tension ksi | 17000 | |
| Modulus of Rigidity ksi | 6400 |
| ALLOY | JOINING TECHNIQUE | SUITABILITY LEVEL |
| C11000 | Soldering | Excellent |
| Brazing | Good | |
| Oxyacetylene Welding | Not Recommended | |
| Gas Shielded Arc Welding | Fair | |
| Coated Metal Arc Welding | Not Recommended | |
| Spot Weld | Not Recommended | |
| Seam Weld | Not Recommended | |
| Butt Weld | Good | |
| Capacity for Being Cold Worked | Excellent | |
| Capacity for Being Hot Formed | Excellent | |
| Forgeability Rating | 65 | |
| Machinability Rating | 20 | |
| FORM | TEMPER | TENSILE STRENGTH | YS-0.5% EXT (KSI) | ELONGATION (%) | ROCKWELL (B) | ROCKWELL (F) | ROCKWELL (30T) | SHEAR STRENGTH (KSI) | TORSION MODULUS (KSI) | IZOD (ft-lbs) | FATIGUE STRENGTH | TENSILE STRENGTH IN SHEAR | SECTION SIZE (IN) |
| PLATE SHEET STRIP BUS BAR | H02 | 42 | 36 | 14 | 40 | 84 | 50 | 26 | 13 | 0.04 | |||
| H01 | 38 | 30 | 35 | 25 | 70 | 25 | 25 | 0.025 | |||||
| H01 | 38 | 30 | 25 | 25 | 70 | 36 | 25 | 0.04 | |||||
| H00 | 36 | 28 | 40 | 10 | 60 | 25 | 0.025 | ||||||
| H00 | 36 | 28 | 30 | 10 | 60 | 25 | 25 | 0.04 | |||||
| M20 | 32 | 10 | 50 | 40 | 22 | 0.025 | |||||||
| M20 | 34 | 10 | 45 | 45 | 23 | 0.04 | |||||||
| H10 | 57 | 53 | 4 | 62 | 95 | 64 | 29 | 0.04 | |||||
| H04 | 50 | 45 | 12 | 28 | 0.24 | ||||||||
| H04 | 50 | 45 | 6 | 50 | 90 | 57 | 28 | 28 | 0.04 | ||||
| H04 | 45 | 40 | 20 | 45 | 85 | 26 | 1 | ||||||
| H04 | 50 | 45 | 12 | 50 | 90 | 28 | 0.025 | ||||||
| OS025 | 34 | 11 | 45 | 45 | 23 | 11 | 0.04 | ||||||
| OS050 | 32 | 10 | 50 | 40 | 22 | 0.025 | |||||||
| OS050 | 32 | 10 | 45 | 40 | 22 | 0.04 | |||||||
| H08 | 55 | 50 | 4 | 60 | 94 | 63 | 29 | 14 | 0.04 | ||||
| ROUND BAR ROD | M20 | 32 | 10 | 55 | 40 | 22 | 1 | ||||||
| H04 | 48 | 44 | 16 | 47 | 87 | 27 | 17 | 1 | |||||
| H04 | 45 | 40 | 20 | 45 | 85 | 26 | 6.4 | 32 | 2 | ||||
| H04 | 55 | 50 | 10 | 60 | 94 | 29 | 0.25 | ||||||
| OS050 | 32 | 10 | 55 | 40 | 22 | 1 | |||||||
| SHAPES PIPE | M30 | 32 | 10 | 50 | 40 | 22 | 0.5 | ||||||
| M20 | 32 | 10 | 50 | 40 | 22 | 0.5 | |||||||
| H04 | 40 | 32 | 30 | 35 | 26 | 0.5 |
Copper 110 has an extremely wide range of applications based on its conductivity, corrosion resistance, workability, and beauty. Some common applications of C11000 Copper include: