EN 1.4659 Stainless Steel Sheet & Plates SS Plate X1CrNiMoCuNW24-22-6 Stainless Steel Data Sheet
Quick Informations
| Products Name | 1.4659 Stainless Steel Plate | Standard | EN 10088-2 |
| Thickness | 0.4 - 40.0mm | Surface | 2B NO.1 BA NO.4 8K |
| Standard Size | 1219*2438mm 1500*6000mm | Service | Cutting, surface processing |
More Informations of our Products
| Item | Stainless Steel Plates / Stainless Steel Sheets |
| Main Grades | 201, 202, 301, 304, 304L, 310S, 309S, 316, 316L, 321, 409L, 410, 410S, 420, 430, 904L, etc. |
| Standard | ASTM GB JIS EN DIN BS |
| Thickness | 0.4mm-40mm |
| Stock Thickness | 0.4mm 0.5mm 0.6mm 0.8mm 1.0mm 1.2mm 1.5mm 2mm, 2.5mm, 3mm, 3.5mm, 4mm, 4.5mm, 5mm, 5.5mm, 6mm, 7mm, 8mm,10mm,12 - 40mm |
| Width | 1000mm 1219mm 1500mm or cutting any size as request |
| Standard size | 1000*2000mm 1219*2438mm 1500*6000mm 2000*6000mm |
| Finish | 2B, BA, No. 1, No. 4, mirror, brush, hairline, chequered, embossed, etc. |
| Package | Standard export package |
EN 1.4659 (X1CrNiMoCuNW24-22-6) Stainless Steel
EN 1.4659 stainless steel is a superaustenitic (highly alloyed) stainless steel formulated for primary forming into wrought products. Cited properties are appropriate for the solution annealed (AT) condition. 1.4659 is the EN numeric designation for this material. X1CrNiMoCuNW24-22-6 is the EN chemical designation.
It has the highest ductility among wrought superaustenitic stainless steels. In addition, it has a very high tensile strength and a moderately high base cost.
The graph bars on the material properties cards below compare EN 1.4659 stainless steel to: wrought superaustenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Among wrought stainless steels, the composition of EN 1.4659 stainless steel is notable for including tungsten (W) and containing a comparatively high amount of manganese (Mn). Tungsten interacts with other alloying elements to a greater extent than usual, which makes it hard to broadly characterize its effects. Manganese is used to improve ductility at elevated temperatures. It also permits a higher nitrogen content than would otherwise be possible.
| Grade | C | Si | Mn | P | S | Cr | Ni | Mo | N | Cu |
| EN 1.4659 | 0.02 | 0.70 | 2.00-4.00 | 0.03 | 0.01 | 23.00-25.00 | 21.00-23.00 | 5.50-6.50 | 0.35-0.50 | 1.00-2.00 |
Mechanical Properties of 1.4659 Stainless Steel
| Grade | Yield / Mpa | Tensile / Mpa | Elongation A(%) | Brinell Hardness(HBW) |
| EN 1.4659 | 684 | 191 | 34 | 444 |
Standard Size of our 1.4659 Stainless Steel Sheets & Plates
| Cold Rolled 1.4659 Stainless Steel Sheets | |||||
| 0.4*1000*2000mm | 0.5*1000*2000mm | 0.6*1000*2000mm | 0.8*1000*2000mm | 1.0*1000*2000mm | 1.2*1000*2000mm |
| 1.5*1000*2000mm | 2.0*1000*2000mm | 2.5*1000*2000mm | 3.0*1000*2000mm | ||
| 0.4*1219*2438mm | 0.5*1219*2438mm | 0.6*1219*2438mm | 0.8*1219*2438mm | 1.0*1219*2438mm | 1.2*1219*2438mm |
| 1.5*1219*2438mm | 2.0*1219*2438mm | 2.5*1219*2438mm | 3.0*1219*2438mm | ||
| 0.8*1500*3000mm | 1.0*1500*3000mm | 1.2*1500*3000mm | 1.5*1500*3000mm | 2.0*1500*3000mm | 2.5*1500*3000mm |
| 3.0*1500*3000mm | 4.0*1500*3000mm | 5.0*1500*3000mm | |||
| Hot Rolled 1.4659 Stainless Steel Plates | |||||
| 4.0*1500*6000mm | 5.0*1500*6000mm | 6.0*1500*6000mm | 8.0*1500*6000mm | 10.0*1500*6000mm | 12.0*1500*6000mm |
| 14.0*1500*6000mm | 16.0*1500*6000mm | 18.0*1500*6000mm | 20.0*1500*6000mm | 22.0*1500*6000mm | 25.0*1500*6000mm |
| 30.0*1500*6000mm | 35.0*1500*6000mm | 40.0*1500*6000mm | 45.0*1500*6000mm | 50.0*1500*6000mm | 55.0*1500*6000mm |
Advantage of our company