ASTM A276 UNS S41000 Stainless Steel Round Bar Diameter 6 - 300mm Alloy 410 Stainless
| Item | Stainless steel round bar | |
| Steel grade | 200/300/400 series | |
| Standard | ASTM A213,A312,ASTM A269,ASTM A778,ASTM A789,DIN 17456, DIN17457,DIN 17459,JIS G3459,JIS G3463,GOST9941,EN10216, BS3605, GB13296 | |
| Material | 304,304L,309S,310S,316,316Ti,317,317L,321,347,347H,304N,316L, 316N,201, 202 | |
| Surface | Polishing,annealing,pickling,bright | |
| Type | hot rolled and cold rolled | |
| Delivery time | Prompt delivery or as the order quantity. | |
| Package | Standard export seaworthy package,or as required. | |
| Application | Widely used in petroleum,foodstuff,chemical industry,construction, electric power,nuclear,energy,machinery,biotechnology,paper making,shipbuilding,boiler fields. Pipes also can be made according to the customer's required. | |
410 stainless steel is hardenable martensitic stainless steel containing at least 11.5% chromium, which provides good corrosion resistance properties. 410 grade offers high strength and hardness with a moderate level of corrosion resistance, however, the corrosion resistance can be further enhanced by a series of processes such as hardening, tempering and polishing. Quenching and tempering can harden grade 410 steel.
410 stainless steel is the basic martensitic stainless steel suitable for highly stressed parts where corrosion resistance, good strength, and ductility are needed. 410 alloy can be used up to 1200ºF (649ºC) where resistance to scaling and oxidation is required. It is used for cutlery applications, kitchen utensils and hand tools and is magnetic in both the annealed and hardened conditions.
The chemical composition of 410 stainless steel contains 11.5–13.5% chromium (Cr) and iron, high carbon content (max 0.15%), and with less nickel content (0.50% Max).
| C | Mn | Si | P | S | Cr | Ni | Iron | |
|---|---|---|---|---|---|---|---|---|
| 410 | 0.08-0.15 | 1.00 Max | 1.00 Max | 0.04 Max | 0.03 Max | 11.5 – 13.5 | 0.50 Max | Bal. |
| Grade | Tensile Strength Ksi (MPa) Min | Yield Strength 0.2% Offset Ksi (MPa) Min | Elongation (% In 50mm) Min | Hardness (Brinell) MAX | Hardness (Rockwell B) MAX |
|---|---|---|---|---|---|
| 410 | 65 (450) | 30 (205) | 20 | 217 | 96 |