T2 Copper Plate Sheet Thickness 0.5 - 60.0mm Custom Cutting Red Copper Plate
| Product name | Copper Plate & Sheet |
| Copper and copper alloy grade | C11000,C10100,C12200 H59, H60, H62, H65, H68, H70, H80, H85, H90, H96, C2100, C2200,C2300, C2400, C2600, C2680, C2720, C2800, C3560, C3601, C3713, C3771, C3561 , CuZn30, CuZn32, CuZn35, CuZn37, CuZn40 ,TU1, T2, TP2, H96, H90, H85, H80, H70, H65, H63, H62, H59, HPb63-3, HPb66-0.5, HPb62-2, HPb62-3, HPb59-3, HSn70-1, HSn62-1,QSn8-0.3, QSn4-4-4, QAl9-4, QSB-1 etc. |
| Width | Within 1500mm Custom Cutting any width as request |
| Thickness | 0.5 - 60.0mm |
| Length | 1m 2m 3m 6m or custom cutting any length as request |
| Standard | ASTM EN DIN JIS GB |
| Other products | Plate, Sheet, Coil , Pipe, Round Bar, Square Bar, Flat Bar, Hexagonal Bar.etc |
What Is T2 Copper?
T2, referred to as copper. A grade of pure copper in machinery, T2 copper refers to a copper-silver alloy, in which the copper + silver element content of copper is >99.9%, and there is no requirement for phosphorus.
Pure copper strip (hard, ≥0.3mm)
T2 conductivity ≥56Ms/m,
Resistance ≤0.0178×10-6 Ω.m.
Brand number: T2
Executive standard: GB/T 2059-2017
Density: 8.9 g/cm³
It has good electrical conductivity, thermal conductivity, corrosion resistance and processing properties, and can be welded and brazed. Contains less impurities that reduce electrical conductivity and thermal conductivity. A trace amount of oxygen has little effect on electrical conductivity, thermal conductivity and processing performance, but it is easy to cause “hydrogen disease”. It is not suitable for processing (annealing, annealing, Welding, etc.) and use.
Used as electrical, thermal, and corrosion resistant equipment. Such as wires, cables, conductive screws, detonators for blasting, evaporators for chemical industry, storage and various pipelines.
Product mechanical properties
Sample size: thickness ≥ 0.2
Tensile strength σb(Mpa): ≥195
Vickers hardness: ≤70HV
Tensile mechanical properties of strip at room temperature
Casting method of product delivery status
Product heat treatment specification and metallographic structure
Heat treatment specification: hot working temperature 900～1050℃; annealing temperature 500～700℃; cold work hardened copper recrystallization starting temperature 200～300℃.
| Copper + silver CUAG (%): ≥99.90 | Beryllium SB (%): ≤0.002 |
| Tin SN (%): ≤0.002 | Sulfur S (%): ≤0.005 |
| Zinc ZN (%): ≤0.005 | Arsenic AS (%): ≤0.002 |
| Lead PB (%): ≤0.005 | Bismuth BI (%): ≤0.001 |
| Nickel NI (%): ≤0.005 | Oxygen O (%): ≤0.06 |
| Iron FE (%): ≤0.005 | Others (%): ≤0.1 (impurities) |
The heat treatment state of the material is different, and the mechanical properties are also different, please refer to the following table:
| Grade | Status | Thickness/mm | Tensile Strength | Elongation(%) | Vickers Hardness HV( HV) |
| (MPa) | |||||
| T2 ,T3 | M (soft) | ≥0.2 | ≥195 | ≥30 | ≤70 |
| TU1,TU2 | Y4 (1/4 hard) | 215~275 | ≥25 | 60~90 | |
| TP1,TP2 | Y2 (semi-hard) | 245~345 | ≥8 | 80~110 | |
| Y (hard) | 295~380 | ≥3 | 90~120 | ||
| T (extra hard) | ≥350 | — | ≥110 |