Flat UNS C11000 Copper Plate Sheet Electrolytic Tough Pitch Copper
UNS C11000 electrolytic tough pitch copper is ductile, has excellence resistance to corrosion, and has a conductivity of 101% IACS. The following datasheet will discuss in detail about UNS C11000 electrolytic tough pitch copper.
Products Specification
| Material | Copper and Copper alloy products | |
| Grade | ASTM | C10100,C11000,C12200,C21000,C22000,C23000,C24000,C26000, C27000,C26800,C27200,C27400,C28000,C36500,C33000,C35300, C35600,C36000,C38500,C44300,C46400,C52100,C54400,C62300, C65500,C67500,C67600,C86300,C90700,C93200,C95400 etc. |
| G/B | TU1,T2,TP2,H96,H90,H85,H80,H70,H65,H63,H62,H59,HPb63-3, HPb66-0.5,HPb62-2,HPb62-3,HPb59-3,HSn70-1,HSn62-1,QSn8-0.3, QSn4-4-4,QAl9-4,QSB-1 etc. | |
| JIS | C 1011,C 1100,C 1220,C3604,C 2100,C 2200,C 2300,C 2400, C 2600, C 2700,C 2680,C 2720,C 2800,C 4430,C 4640,C 5210, C 5441, CAC304 etc | |
| BS | Cu-OFE,C 101,Cu-DHP,CZ 125,CZ 101,CZ 102,CZ 103,CZ 106,CZ 107, CZ 108,CZ 109,CZ 123,CZ 124,CZ 121,CZ 111,CZ 133, Pb 104, CS 101, CuSn10P etc. | |
| DIN/ISO | CuZn5,CuZn10,CuZn15,CuZn20,CuZn30,CuZn35,CuZn33,CuZn36, CuZn37,CuZn40,CuZn40Pb,CuZn37Pb2,CuZn36Pb3,CuZn39Pb3, CuZn28Sn1,CuZn38Sn1,CuSn8,CuSn4Pb4Zn3,CuSi3Mn,CuZn25Al5, CuSn10, CuSn7Zn3Pb7 etc. | |
| Shape | Round, Square, Flat, Hexagon, Oval, Half-round or Customized | |
| Dimension | Bar/Rod | Standard(Diameter 5-160 mm) or Customized |
| Wire | Standard(Diameter 0.02-6 mm) or Customized | |
| Plate/Sheet | Standard(T 0.2-50 mm/W 200-3000 mm/L 6000 mm) or Customized | |
| Strip | Standard(T 0.05-1.5 mm/W 20-600 mm/L 20000 mm) or Customized | |
| Tube/Pipe | Standard(OD 3-360mm/Wall thickness 0.5-50 mm) or Customized | |
| Standard | GB/T,JIS,ASTM, ISO, DIN, BS, NF etc. | |
| Hardness | 1/16 hard,1/8 hard,3/8 hard,1/4 hard,1/2hard,full hard. | |
| Package | Plastic film + Wooden case or as per customer requirement | |
| Surface | Polished,bright,oiled,hair line,brush,mirror,or as required | |
| Deliver time | According to order's quantity. | |
| Shipment | By sea, by air, DHL, UPS, FedEx etc. or as required | |
| Application | Electric light industry, machinery manufacturing, Building industry ,defense industry, and other fields Manufacturing industrial | |
Chemical Composition of C11000 Copper
The following table shows the chemical composition of UNS C11000 copper.
| Element | Content (%) |
|---|---|
| Cu | 99.90 |
The physical properties of UNS C11000 copper are given in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.89 g/cm3 | 0.322 lb/in3 |
| Melting point | 1065 - 1083°C | 1949°F |
The mechanical properties of UNS C11000 copper are tabulated below.
| Properties | Metric | Imperial |
|---|---|---|
| Hardness, Rockwell F (hard temper) | 80.0 | 80.0 |
| Poisson's ratio | 0.34 | 0.34 |
| Elastic modulus | 115 - 117 GPa | 16969 ksi |
The designations that are equivalent to the UNS C11000 copper are outlined in the following table.
| ASME SB133 | ASTM B173 | ASTM B228 | ASTM B33 | ASTM B49 | ASTM F467 |
| ASTM B1 | ASTM B174 | ASTM B229 | ASTM B355 | ASTM B496 | ASTM F468 |
| ASTM B101 | ASTM B187 | ASTM B246 | ASTM B370 | ASTM B506 | MIL B-20292 |
| ASTM B116 | ASTM B188 | ASTM B272 | ASTM B447 | ASTM B556 | MIL C-12168 |
| ASTM B124 | ASTM B189 | ASTM B283 | ASTM B451 | ASTM B638 | MIL W-6712 |
| ASTM B133 | ASTM B2 | ASTM B286 | ASTM B47 | ASTM B694 | QQ B575 |
| ASTM B152 | ASTM B224 | ASTM B298 | ASTM B470 | ASTM B738 | SAE J461 |
| ASTM B172 | ASTM B226 | ASTM B3 | ASTM B48 | ASTM B8 | SAE J463 |
Welding
Welding techniques such as soldering, brazing, gas shielded arc welding, oxyacetylene welding and butt welding are recommended for C11000 copper. Other welding techniques such as coated metal arc welding, spot welding and seam welding are not preferred.
C11000 copper is forged at hot working temperatures ranging from 760 to 871°C (1400 to 1600°F). The hot forgeability rate of this metal is 65%.
C11000 copper has excellent hot working property.
C11000 copper has excellent cold working property.
Annealing of C11000 copper is performed at temperatures ranging from 371 to 649°C (700 to 1200°F).
UNS C11000 copper is best suited for plumbing fittings and other electrical components that do not require prolonged machining performance.