6m Length 31CrMoV9 / 1.8519 Alloy Steel Round Bar GB Forged Steel Rod
Products Specification
| Products Name | 31CrMoV9 Alloy Steel Round Bar |
| Diameter | 10 - 500 mm |
| Length | 6m or custom cutting any length as request |
| Type | Hot Rolled |
| Brand | BAOSTEEL DELTA DONGBEI HUAXI SHAGANG.etc |
| MOQ | 1 Ton |
| Loading Port | Shanghai Port |
| Packing | packing by steel wire rope |
| Deliver time | 5 - 7 days for stock materials |
| Other Grade | Q195,Q235,10#,20#,35#,45#,Q215,Q345,12Cr1Mov,15CrMo,304,3 16,20Cr,40Cr,20CrMo,35CrMo,42CrMo,40CrNiMo,GCr15,65Mn,50Mn, 50Cr,3Cr2W8V,20CrMnTi,5CrMnMo ,38CrMoAl, 31CrMoV9 |
| Standard | ASTM GB EN DIN |
| Application | Structure and Industrial |
| Standard Diameter | 10 12 15 18 20 25 30 35 40 45 50 55 60 65 70 75 80 85 90 95 100 105 110 120 130 140 150 160 180 200 210 220 230 250 270 300 320 330 350 360 370 380 390 400 410 420 430 440 450 460 470 480 490 500 |
1.Supply Form & Size & Tolerance
| Surface Finish | Tolerance |
| Black For Forged condition | (0,+5mm) |
| Black For Rolled condition | (0,+1mm) |
| Rough Turned | (0,+3mm) |
| Grinding | Best h9 |
| Polished | Best h11 |
| Peeled | Best H11 |
| Cold Drawn | Best H11 |
2.Chemical Composition
| Grade | C | Mn | P | S | Si | V | Cr | Mo |
| 31CrMoV9/1.8519 | 0.27-0.34 | 0.40-0.70 | ≤ 0.025 | ≤ 0.035 | ≤ 0.4 | 0.1-0.2 | 2.3-2.7 | 0.15-0.25 |
3.Physical Property
4. Mechanical Property
| Diameter d mm | 16-40 | 40-100 | 100-160 | 160-250 |
| Yield Strength Mpa | ≥900 | ≥800 | ≥700 | ≥650 |
| Tensile Strength Mpa | 1100-1300 | 1000-1200 | 900-1100 | 850-1050 |
| Elongation, % | ≥9 | ≥10 | ≥11 | ≥12 |
| impact,J | ≥25 | ≥30 | ≥35 | ≥40 |
| Hardness,HB | 331-380 | 298-359 | 271-331 | 253-319 |
5.Forging
Heat the temperature between 1050℃-1150℃,hold suitable time for the steel to be thoroughly heated.Reheat the steel once temperature below 850°C. Crack is easily occured when improper cooling way after forged,so it should be cooled as slowly as possible in the furnace or in sand after forged.
6.Heat Treatment
| Hold time,h | Hardness,HV | ||||||
| 30 | 750 | 540 | 430 | 410 | 400 | 380 | 380 |
| 90 | 830 | 750 | 640 | 530 | 430 | 410 | 410 |
| 120 | 790 | 730 | 660 | 600 | 540 | 460 | 400 |
| 180 | 800 | 760 | 700 | 640 | 580 | 550 | 420 |
| Depth,mm | 0.15 | 0.25 | 0.35 | 0.45 | 0.55 | 0.65 | 1 |
7.Jominy Test -Distance from quenched end mm
| mm | 2 | 8 | 12 | 16 | 20 | 30 | 40 | 50 | 60 | 70 |
| HRC | 51 | 50 | 50 | 49 | 48 | 46 | 44 | 42 | 41 | 41 |
8.Application
31CrMoV9 nitriding steel is used in mechanics automotive and general mechanics, which must be nitrided for very high wear forces, for example, gears, rods or axes.Structural parts of medium and large cross sections and high surface hardness, e.g., valve and gate valves, cylinders for combustion engines, superheated steam valves and fittings.